CHARACTER

a. Short-term aging: 150 ± 3 / 240H after aging, low temperature (-25 ± 2℃ / 4H) winding experiment,The voltage resistance experiment was performed. No visible exposed conductor after winding and should not be penetrated in voltage resistant experiments. Before applying the voltage, the sample shall be soaked in the saline bath for at least 10 min; Apply 1 kV (AC) voltage for 1 min without applying 1kV (AC) voltage.

b. Low-temperature winding resistance: -40 ± 2℃ / 4H, winding the specified number of circles in the freezer. After winding, no visible exposed conductor. Then conduct the voltage resistance experiment, no breakdown.

c. Thermal shrinkage: 150 ± 3℃ / 15min, and the maximum shrinkage of insulation at any end shall not exceed 2mm.

d. Anti-flame retardant: sample 45 degrees dip, apply flame. For wires with a size no greater than 2 . 5 mm2 , After 1 5 s, the flame can be removed, for wires larger than 2.5 mm2, after 30 s To revoke the flame. The combustion flame shall be extinguished within 7 0 s with at least 5 0 m at the sample end Insulation shall remain unburned.

SPECIFICATIONS

Conductor: Tinned /Bare copper 

Insulation materials: PVC Insulation

Rated temperature: -40~105℃

rated voltage: 600Vac or1000Vdc

Reference: DIN 72551 ,ISO6722

Compliance with ROHS / REACH

STRUCTURE

Label identification: manufacturer, model, specification, rated temperature, rated withstand voltage, insulation material, color, packaging length, date of manufacture

Should be used:Apply to road vehicles with thin wall insulation single core no shielding low voltage cables.

Colors Available: BLACK, WHITE, RED, YELLOW, GREEN, BLUE, BROWN, GREY, ORANGE, VIOLET

Suitable for all conventional wire harness processing proc