SGX Wire

Characteristic

excellent mechanical properties: Tensile strength≥10MPa，elongation at break≥150％ After aging： Condition：155±2.0℃/ 168h Tensile strength residual rate≥80% elongation at break≥50％

Flame retardancy：45°suspension, the ignition time is 30 seconds, the sample should not continue to burn for more than 15S after extinguishing, and the unburned portion at the top of the sample should not be less than 50mm.

Low temperature bending：-40±2℃, 3 hours, after low temperature treatment, the sample is wound around the test rod at a uniform speed of 10 seconds per turn, and there are no cracks on the surface of the sample. After returning to room temperature, a voltage resistance test is performed and the insulation does not break down。

Specifications

Conductor: Tinned or Bare copper 

Insulation materials: xlpe Insulation

Rated temperature: 125℃

rated voltage: 25Vac or 60Vdc

Reference:SAE J1127

in line with ROHS/REACH

Colors Available: ten kinds

Structure

Electrical performance

Spark test：When passing through the test electrode, no breakdown occurs. Spark test voltage is 5KV AC。

dielectric withstand voltage：Insulate both ends of the sample, immerse it in a 5% salt solution, with both ends protruding no more than 150mm from the water surface, and soak it for 5 hours. Apply 1000Vrms, 50-60Hz voltage for one minute, and the insulation will not break down。